Big Caliber 92% Alumina Ceramic Tube of Good Resistance

• Application: Metallurgical Machinery, Cement Plant, Mining Machine, Industrial Ceramic
• Ceramic Tube & Rod: Ceramic Tube
• Standard: GB
• Model NO.: ZALY
• Material: Aluminum, Alumina Ceramic
• Al2O3 Content: 92%, 95%, 99%
• Color: White
• Customized Service: Avaliable
• Hardness: 9
• Density: 3.6
• Type: Ceramic Tube, Wear Resistant Pipe, Ceramic Parts
• Transport Package: Standard Export Wooden Box
• Specification: 92%
• Trademark: ZALY
• Origin: Lianyungang, Jiangsu, China
• HS Code: 69091200
• Production Capacity: 3000 PCS/ Month

Product Description

High-purity Big Caliber Alumina Ceramic Tube
Top One Product
It is widely used in some special parts which require high strength,high hardness,heat-resistance,corrosion resistant and wear-resistant.

(1) Big caliber ceramic tube made of 92% alumina is widely used in industry of minning,power,metallurgical,coal,chemical and so on.it works as lining in pipe for transport of powder material and corrosive material, such as sand,ash, slag and chemical.
In some special site where wear plates can not service well, ceramic tube is a perfect substitute. It is a solution to problem of partial wear plate dropping off and has been enjoying high reputation.

(2) Big caliber ceramic tube made of 95% alumina is used as lining of hydraulic cyclone for paper-making and mineral separation.And most ofthe textile ceramic components are made of alumina 95%.

(3) Most of the ceramic spools,structural ceramic components are made of alumina 99%.The future is bright and the consumption quantity is increasing year by year.

 

Table1:Technical Parameter Of Alumina Ceramics
Item	Test condition	Unit&Symbol	95%  Alumina Ceramics	99% Alumina Ceramics	99.7% Alumina Ceramics
The Main Chemical Ingredient			Al2O3	Al2O3	Al2O3
Bulk Density		g/cm³	>3.6	3.89	3.96
Maximum Use Temperature		ºC	1450	1600	1650
Water Absorption		%	0	0	0
ROHS Hardness			≥85	≥ 89	≥89
Flexural Strength	20 ºC	Mpa(psi*10³)	358(52)	550	550
Compressive Strength	20 ºC	Mpa(psi*10³)	2068(300)	2600(377)	2600(377)
Fracture Toughness	K(lc)	Mpa m 1/2	4-5	5.6	6
Coefficient Of Thermal Expansion	25-1000 ºC	1*10 -6 /ºC	7.6	7.9	8.2
Coefficient Of Thermal Conductivity	20 ºC	W/mk	16	30.0	30.4
Thermal Shock Resistance	ΔTc	ºC	250	200	200
Dielectricity Constant	1MHz.25 ºC		9	9.7	9.7
Dielectricity Strength		ac-kV/mm(ac V/mil)	8.3(210)	8.7(220)	8.7(220)
Volumn Resistivity	100 ºC	ohm-cm	>10 13	>10 14	>10 14