92% Alumina Ceramic Hexagonal Tile of Good Wear Resistance

• Classification: Alumina
• Alumina Content: 80%, 92%, 95%, 99%, 99.7%
• Size: Rich
• Model NO.: ZALY
• Raw Material Origin: Australia
• Certifications: SGS, ISO
• Grade Standard: Industrial Grade
• Quality: First Class
• Transport Package: Standard Export Wooden Box
• Trademark: ZALY
• Origin: Lianyungang, Jiangsu, China
• HS Code: 6901000000
• Production Capacity: 30mt Per Month

Product Description

Alumina Wear Tile / Hexagonal Alumina Ceramic Tile & Small Tile
Alumina Ceramic Tile is of high wear resistance, acid and alkli resistance, effectively prolong the service life of equipment and considered to be the best choice of anti-wearing and anti-corrosion material; Wear resistance of ceramic is 266 times than that of special manganese, 171.5 times to high chrome cast iron; Hardness is much higher than that of wear-resistant steel and stainless steel.

Application:
Oil, mining, steel and power industry.

Size Available(mm)( Length x width x height):
25mm x 25mm x 3mm
25mm x 12.5mm x 3mm
50mm x 25mm x 3mm
50 mm x 12.5 mm x 3 mm
25mm x 25mm x 5mm
25mm x 12.5mm x 5mm
50mm x 25mm x 5mm
50mm x 12.5mm x 5mm
25mm X 25mm X 6mm
25mm X 12.5mm X 6mm
50mm X 25mm X 6mm

Trapezoidal Tile: Customized
Hex Mat 150MM x 150MM of 6MM Tile
Hex Mat 150MM x 150MM of 3MM Tile
Hex Tile 1/2" Pieces 6MM
Hex Tile 1/2" Pieces 3MM

 

Table1: Technical Parameter Of Alumina Ceramics
Item	Test condition	Unit& Symbol	95%  Alumina  Ceramics	99% Alumina  Ceramics	99.7% Alumina  Ceramics
The Main Chemical Ingredient			Al2O3	Al2O3	Al2O3
Bulk Density		g/cm³	> 3.6	3.89	3.96
Maximum Use Temperature		º C	1450	1600	1650
Water Absorption		%	0	0	0
ROHS Hardness			≥ 85	≥   89	≥ 89
Flexural Strength	20 º C	Mpa(psi*10³ )	358(52)	550	550
Compressive Strength	20  º C	Mpa(psi*10³ )	2068(300)	2600(377)	2600(377)
Fracture Toughness	K(lc)	Mpa m 1/2	4-5	5.6	6
Coefficient Of Thermal Expansion	25-1000 º C	1*10 -6 /º C	7.6	7.9	8.2
Coefficient Of Thermal Conductivity	20 º C	W/mk	16	30.0	30.4
Thermal Shock Resistance	Δ Tc	º C	250	200	200
Dielectricity Constant	1MHz. 25 º C		9	9.7	9.7
Dielectricity Strength		ac-kV/mm(ac V/mil)	8.3(210)	8.7(220)	8.7(220)
Volumn Resistivity	100 º C	ohm-cm	> 10 13	> 10 14	> 10 14