Yttria Stabilized Zirconia Grinding Media

• Material: Zirconia
• Content: >90%
• Usage: Grind
• Model NO.: TCH-Zirconia
• Processing Type: Rolling Type
• Size: Small
• Color: White
• Customized: Customized
• Shape: Ceramic Balls, Ceramic Cylinder,Ceramic Beads
• Application: Industrial Ceramic
• Transport Package: Standard Export Carton, Loaded on The Pallet
• Specification: SGS
• Trademark: ZALY
• Origin: China
• HS Code: 690919000
• Production Capacity: 100ton/Month

Product Description

Product Description
This is  Y-TZP yttria stabilized zirconia grinding media, which is made of top quality zirconia powder, suitable for any kinds of mills such as ball mill, sand mill, attritor mill and vibratory mill.
 
Applications
Electronics Industry: Piezoelectric ceramics, inductance materials, capacitors ceramics, semiconductor ceramics, etc..
Battery Industry: Lithium iron phosphate, cobalt acid lithium materials, etc..
Chemical Industry: Paint, materials, printing ink, pigments, etc..
Ceramic Industry: Refractory materials, glaze materials, silicic acid zirconia, structural ceramics, etc..
Other Industry: Food, Medicine, Cosmetics
 
Features
1. Glossy satin smooth surface
2.  Excellent tanacity & impact-resistance, making the beads keep fine in high rotation speed
3. Low friction coefficient makes lower abrasion to the equipment.
4. Y-TZP grinding media is over 30-50 times longer life than glass beads
5. Y-TZP grinding media is 5 times longer life than zirconium silicate beads.
6. Higher density than other grinding media
7. Y-TZP's grinding efficiency is 6-8 times than glass beads, 2-3 times than zirconium silicate beads.
Specifications
 

Composition (Wt%)	94.8+0.2% ZrO2, 5.2+0.2% Y2O3
Specific density (g/cm3)	≥6.0
Hardness HV (Gpa)	>12
Bending Strength (Mpa)	1150
Fracture toughness (Mpa·m1/2)	>9
Grain size (µm)	≤0.5
Elastic modulus (Gpa)	200
Thermal conductivity (W/m.k)	3 (20-400°C_
Coefficient of thermal expansion (10-6K-1)	9.6 (20-400°C)